This study aims to investigate the properties of mortar made from a bottom ash substitute as a sustainable construction material. It is believed that the use of cement in concrete construction contributes to the release of carbon dioxide into the atmosphere, which has been a consistent increase in recent years. The utilization of bottom ash waste is expected to reduce pollution associated with cement production.

Bottom ash is used as replacement materials for cement and fine aggregate in the manufacture of mortar. Bottom ash substituted for cement of 10%, 20% and 30% of the total weight of the binder, whereas bottom ash substituted for the fine aggregate of 30%, 40% and 50% of the total weight of the sand. Binder properties were determined using scanning electron microscopy and energy dispersive X-ray. Meanwhile, the fresh properties (slump flow) and hardened properties were determined (compressive strength and mass density). In the hardened properties test, two types of curing were used: water and sealed curing.

The compressive strength of mortar decreased as the amount of bottom ash as cement replacement. However, the compressive strength increased when bottom ash was used as aggregate replacement. Additionally, bottom ash was sufficient as a substitute for fine aggregate than as a substitute for cement.

This research presents test results that are more straightforward to apply in the construction site.

This study aims to discuss the results of fresh properties and compressive strength of self-compacting concrete using ingredients added red brick powder as a fine aggregate substitute. The results of the study were compared with the properties of fresh properties and compressive strength with ingredients added by rice husk ash, which is also a fine aggregate substitute. In addition, the initial compressive strength of each of these variations was also examined to accelerate the completion time of construction projects using self-compacting concrete.

This research was conducted in a laboratory by testing the characteristics of fresh and hardened properties of self-compacting concrete.

Fresh properties testing is carried out in the form of V-funnel, flow table, J-ring and L-box where all specimens produce quite varied flow rates. Compressive strength was estimated at ages 3, 7, 14 and 28 days with cylindrical specimens with a diameter of 150 mm and a height of 300 mm. The variation of fine aggregate substitutes used is 20, 40 and 60 per cent.

From the results of the compressive strength, it can be concluded that the added material is categorized as self-compacting concrete with high initial compressive strength, while at 28 days, the compressive strength test results are categorized as high-strength self-compacting concrete.

This study aims to investigate the size effect of the patched repairing material applied to the cracked beam.

Numerical analysis was conducted on a simply supported cracked beam with a dimension of 200 × 25 × 15 cm using ABAQUS software. The behavior of concrete and engineered cementitious composites (ECC) in the simulation are described as concrete damage plasticity model. Linear elastic-plastic model was used to represent the behavior of rebar steel. The type of patching consisted of the varying ratio of lengths and depths, including patching length to total length ratios of 0.2, 0.3 and 0.4, and patching depth to total depth ratios of 0.2, 0.3, 0.4 and 0.5.

Results show that variations in the patching length and depth ratios affect the maximum flexural load, stiffness and ductility of the repaired beam. It was also found that repairing the cracked beam by using ECC provides higher flexural load of the beam than the use of conventional concrete, owing to the superior tensile strength of ECC.

ECC is the cementitious-based mortar that contains the special selected poly vinyl alcohol fiber having high tensile strength. ECC has been known to exhibit high ductility, high tensile strength and improve durability performance. Thus, ECC is suitable as repairing material for patching cracked beam. By investigating the size of the patched repairing material applied to the cracked beam, the structural performance of repairing beam and the effectiveness of the various patching size were achieved.